Esem Study of Oil Wetting Behaviour of Polypropylene Fibres
Étude ESEM de la mouillabilité des fibres de polypropylène par l'huile
1
Heriot-Watt University Scottish, Borders Campus, Galashiels TD1 3HF - United Kingdom
2
Heriot-Watt University, Institute of Petroleum Engineering, Edinburgh, EH14 4AS - United Kingdom
Corresponding author: q.wei@hw.ac.uk
Polypropylene (PP) fibres have been increasingly used in oil related areas, such as oil sorbents, oil coalescers, oil filters and oil separators. The wetting behaviour of the fibres by oil is of particular importance in these applications. The environmental scanning electron microscope (ESEM) technique was used in this study to investigate the oil wetting of polypropylene fibres. The wettability was investigated by contact angle measurements with oil. Oil drops were added onto fibres using a micro-injector. The contact angles were measured from ESEM micrographs using image analysis and theoretical approach. ESEM observation reveals the wetting of single fibres on a microscopic level.
Résumé
Les fibres de polypropylène ont été utilisées de manière conséquente dans les domaines relatifs à l'huile tels que les matériaux absorbants et coalescents à l'huile, les filtres à huile et les séparateurs d'huile. La mouillabilité des fibres par l'huile est particulièremement importante dans ces applications. La technique du microscope environmental scanning electron (ESEM) a été utilisée dans cette étude afin de comprendre la mouillabilité des fibres de polypropylène par l'huile. La mouillabilité a été observée par des mesures d'angle de contact avec l'huile. Les gouttes d'huile ont été ajoutées sur les fibres à l'aide d'une micro-pipette. Les angles de contact ont été mesurés à partir d'un micrographe ESEM utilisant l'analyse de l'image et l'approche théorique. L'observation ESEM révèle des fibres individuelles au niveau microscopique.
© IFP, 2003