EXAFS Characterization of New Active Phases for Catalytic Hydrotreatment: Two Cations Disulfide Layers in the Mo_xW_(1-x)S₂ Lamellar Solid Solution

Caractérisation par EXAFS de nouvelles phases actives pour l'hydrotraitement catalytique : les couches disulfures à deux cations de la solution solide lamellaire Mo_xW_(1-x)S₂

¹ IFP-Lyon, BP 3, 69390 Vernaison - France
² IRC-CNRS, 2 avenue Albert Einstein, 69626 Villeurbanne - France
³ IMJR, UMR 6502, CNRS-Univ. Nantes, 2 rue de la Houssinière, 44322 Nantes - France

Corresponding author: cecile.thomazeau@ifp.fr

Abstract

Synchrotron and Neutron Solutions to Oil Industry ProblemBulk and alumina-supported Mo_0.5W_0.5S₂ compounds were prepared. The presence of both molybdenum and tungsten in every [MS₂] layer (intralayer solid solution) was evidenced using EXAFS spectroscopy, the only local method which can provide such relevant structural information. The catalytic interest of such solid solution is to provide a continuous variation of M-S bond strength which is considered as the key parameter of the catalytic activity transition metal sulfides. The solid solution is maintained after promotion by Ni either on unsupported or supported state.

Résumé

Des composés Mo_0.5W_0.5S₂ ont été préparés à l'état massique et à l'état dispersé sur alumine. L'absorption X, seule technique permettant d'obtenir cette information, montre que les deux cations Mo et W sont présents au sein de chaque couche [MS₂], selon un modèle de solution solide intrafeuillet. L'intérêt de ce système mixte est de pouvoir moduler la force de liaison Métal-Soufre considérée comme le paramètre clé de l'activité catalytique des sulfures de métaux de transition. Cette solution solide est toujours présente après promotion par le Ni des systèmes massiques ou supportés sur alumine.